Property | Value | Method |
---|---|---|
Tensile Properties | ||
Young’s Modulus | 2.4 +/- 0.2 GPa | ASTM D638 |
Ultimate Tensile Strength | 69 +/- 1 MPa | ASTM D638 |
Elongation at Break | > 20% | ASTM D638 |
Tensile Toughness | > 15 MPa | ASTM D638 |
Flexural Properties | ||
Flexural Modulus | 1.8 +/- 0.1 GPa | ASTM D790 |
Ultimate Flexural Strength | 53 +/- 1 MPa | ASTM D790 |
Thermal Properties | ||
Glass Transition Temperature (Tg) | ||
Tg by DSC | 164 +/- 3 °C | ASTM E1356 |
Tg by Peak of Loss Modulus Curve at 1 Hz | 152 °C | D4065 |
Heat Deflection Temperature (HDT) | ||
HDT Method A: 0.455 MPa | 139 °C | ASTM E2092 |
HDT Method B: 1.82 MPa | 132 °C | ASTM E2092 |
Impact Strength | ||
Un-notched IZOD | > 800 J/m | |
Notched IZOD | 34 +/- 2 J/m | ASTM D256 |
Hardness | ||
Shore D Hardness | 84 +/- 1 D | D2240 |